Submerged arc welding technology is the welding process of SSAW steel pipe and LSAW steel pipe. During the welding process, in addition to insufficient penetration, burn-through and poor formation caused by improper welding process parameters, there will also be pores, slag inclusions, cracks, etc. Defects. This article mainly introduces the main reasons and preventive measures for porosity in submerged arc welding seams. (1) In the process of steel rolling or hot stamping and coiling, the oxide scale formed or fallen off, as well as the positioning welding slag shell, the carbon arc gas created flying slag, etc., are trapped in the flux, which will also cause pores in the weld. Preventive measures: ①The oxide skin that falls off during the process of coiling and bending should be cleaned or blown off with compressed air before assembly and welding to prevent it from being caught in the assembly gap or falling into the groove. ②The surrounding of the welding site should be clean t...